Conditions And Terms Of Supply

Share
Conditions And Terms Of Supply

HANDLING INSTRUCTIONS FOR GLASSWARE

*Download PDF of this page in English and French by clicking this link

IMPORTANT INFORMATION:

  • All heavy sham (thick base) and oversized glassware must be handled with cared due to the very nature of the glass.
  • The thick sham (base) will always retain heat longer than the thinner sides of the glass.
  • Touch a warm glass on the side and then the base. You will notice how much warmer the base is.
  • The base always cools off slower than the balance of the glass.
  • Although you may think the glass is at room temperature, it isn’t thoroughly.
  • All glassware is subjected to ASTM testing regulations at the time of manufacture.
  • glassware manufactured for the purpose of holding hot beverages are considered to hold beverages at a maximum temperature of 65 degrees celcius.
  • Glassware manufactured for the purpose of holding cold beverages are considered to hold beverages at a maximum low temperature of 6 degrees celcius.
  • All glassware is rated for a regulated, controlled temperature change of 42 degrees. Sudden and rapid temperature changes ar to be avoided as breakage can occur.

CARE INSTRUCTIONS FOR YOUR GLASSWARE:

  • Ensure the glassware is at room temperature prior to use. Use double the time of a regular glass cooling, as a rule of thumb.
  • Do not store or place the glassware in a glass chiller, freezer or fridge.
  • Whenever possible use a glass rack or store on trays.
  • Whenever possible, wash glassware early in the morning or evening to allow sufficient cooling time.
  • Never smash or stack glassware when clearing tables.
  • Do not put cutlery into glassware when clearing the tables.
  • Ensure proper washing temperatures in your glass washers.
  • Ensure you have sufficient glassware to permit proper cooling times.
  • Never pour cold beer in a warm glass.
  • Never pour cold beer in a glass directly out of the glass washer.

* ALL GLASSWARE PRODUCED BY ZENAN CUSTOM CRESTING MUST BE WASHED IN A DISHWASHER PRIOR TO FIRST USE.

CAUSES FOR FREQUENT BREAKAGE:

  • Mechanical Impact
  • Result of impact against other objects including: Other glassware / Loading and unloading of dishwasher /
    / Bussing of tables-cutlery dropped in glassware / Draft beer pour
    Taps and sinks
  • Thermal Shock – Rapid change in temperature of more than 42 Degrees Celcius. when an article of glass passes from cold to hot, or vice versa.

Causes_for_breakage

 

POSSIBLE GLASS FAILURE DUE TO THERMAL SHOCK:

  • Thermal shock is the name given to cracking as a result of rapid temperature change. Glass and ceramic objects are particularly vulnerable to this form of failure, due to their low toughness, low thermal conductivity, and high thermal expansion coefficients.
  • Thermal shock can be prevented by reducing the thermal gradient seen by the object, by changing its temperature more slowly.
  • Thermal shock occurs when a thermal gradient causes different parts of an object to expand by different amounts. This differential expansion can be understood in terms of stress or strain, equivalently. At some point, this stress overcomes the strength of the material, causing a crack to form.
  • Thermal shock describes the way in which some materials are prone to damage if they are exposed to a sudden change in temperature. Glass and certain other materials are vulnerable to this process, in part because they do not conduct thermal energy very well. This is readily observed when a hot glass is exposed to ice water – the result is cracked, broken, or even shattered glass.thermal shock is a reaction to a rapid and extreme temperature fluctuation, but the process is somewhat more complicated than this. The shock is the result of a thermal gradient, which refers tot he fact that temperature change occurs in an uneven fashion. Temperature change causes expansion of the molecular structure of an object, due to weakening of the bonds which hold the molecules in formation. The existence of the thermal gradient means this expansion occurs unevenly, and glass in particular is very vulnerable to this process.

* ZENAN WILL NOT ACCEPT RESPONSIBILITY FOR BREAKAGE DUE TO THERMAL SHOCK, OR BREAKAGE CAUSED BY CONSUMER IMPROPER HANDLING OF GLASSWARE.

*Download PDF of this page in English and French by clicking this link